Crosslinkable Propylene-Based Copolymers, Methods for Preparing the Same, and Articles Made Therefrom

ABSTRACT

Provided are crosslinkable propylene-based copolymers, methods for making the same, elastomeric compositions including the same, and articles made therefrom, e.g., films and fibers. Exemplary elastomeric compositions are composed of at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; about 0.5 wt % to about 10 wt % vinyl siloxane; and about 0.1 wt % to about 1.0 wt % peroxide. The elastomeric compositions can be extruded and crosslinked at a temperature of at least about 50° C. and a relative humidity of at least about 90% to provide a crosslinked elastomeric composition. The crosslinked elastomeric compositions are particularly useful for making fibers and films.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the priority benefit of Provisional Application No. 61/227,846, filed Jul. 23, 2009, the disclosures of which are incorporated by reference in their entireties.

FIELD OF THE INVENTION

Provided are crosslinkable propylene-based copolymers, methods for making the same, elastomeric compositions including the same, and articles made therefrom. More particularly, embodiments of the present invention relate to fibers and films produced from crosslinked propylene-based polymers.

BACKGROUND OF THE INVENTION

Materials with good stretchability and elasticity are used to manufacture a variety of disposable articles in addition to durable articles including incontinence pads, disposable diapers, training pants, clothing, undergarments, sports apparel, automotive trim, weather-stripping, gaskets, and furniture upholstery. For clothing, stretchability and elasticity are performance attributes that allow the materials to provide a closely conforming fit to the body of the wearer.

While numerous materials are known to exhibit excellent stress-strain properties and elasticity at room temperatures, it is often desirable for elastic materials to provide a conforming or secure fit during repeated use, during extensions and retractions at elevated or depressed temperatures, or in automobile interiors during summer months. Elasticity at elevated temperatures is also important for maintaining tight tolerances throughout temperature cycles. In particular, elastic materials used for repeated wear clothing or garments must maintain their integrity and elastic performance after laundering.

Spandex™, a segmented polyurethane urea elastic material, is currently used in various durable fabrics. For example, fibers made from Spandex™ have been used in launderable apparels, fabrics, durable and disposable furnishing, beddings, etc. Similar to conventional uncrosslinked polyolefin-based elastic materials, articles made from Spandex™ can lose integrity, shape, and elastic properties when subjected to elevated temperatures. Thus, Spandex™ may not be suitable for many co-knitting applications with high temperature fibers, such as polyester fibers.

Accordingly, there is still a need for new and improved propylene-based materials and articles therefrom, such as fibers and films, of elastic polyolefins that have good thermal resistance, stretchability, and elasticity.

SUMMARY OF THE INVENTION

Provided are crosslinkable propylene-based copolymers, methods for making the same, elastomeric compositions including the same, and articles made therefrom, e.g., films and fibers. Preferably, method includes blending an elastomeric composition comprising at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; about 0.5 wt % to about 10 wt % vinyl siloxane; and about 0.1 wt % to about 1.0 wt % peroxide. The blended composition can be extruded and crosslinked at a temperature above 30° C. and a relative humidity of 50% or above 50° C. and a relative humidity of 90%.

In alternative embodiments, the method includes blending an elastomeric composition comprising at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; one or more polyolefinic thermoplastic components; about 0.5 wt % to about 10 wt % vinyl siloxane; about 0.1 wt % to about 1.0 wt % peroxide; and about 0.01 wt % to about 5 wt % condensation catalyst. The blended composition can be extruded and crosslinked at a temperature of at least about 30° C. and a relative humidity of at least about 50% or at least about 50° C. and a relative humidity of at least about 90%.

In other alternative embodiments, the crosslinked elastomeric composition can include of from about 51 wt % to about 90 wt % at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; of from about 0.5 wt % to about 10 wt % vinyl siloxane; of from about 0.1 wt % to about 1.0 wt % peroxide; of from about 5 wt % to about 40 wt % one or more polyolefinic thermoplastic components; and optionally of from about 5 wt % to about 40 wt % one or more secondary elastomeric components, wherein the crosslinked polypropylene has greater than 50% xylene insolubles as measured according to ASTM-D 5492.

It has been found that propylene-based polymers and blends thereof can be grafted with hydrolysable silane moieties that can be further crosslinked through condensation reactions. These compositions are suitable for preparing crosslinked articles with improved elastic and thermal performance compared to the uncrosslinked compositions.

In one or more embodiments, the propylene-based polymers and blends thereof are surprisingly crosslinkable at a temperature of at least about 30° C. and a relative humidity of at least about 50% or above at least about 50° C. and a relative humidity of at least about 90%. In a particular embodiment, the crosslinking is accomplished by exposing the elastomeric composition to water (“moisture cure”).

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

References below to the “invention” may in some cases refer only to certain specific embodiments only. In other cases it will be recognized that references to the “invention” will refer to subject matter recited in one or more, but not necessarily all, of the claims.

The propylene-based polymer is composed of one or more propylene-α-olefin-diene terpolymers or propylene-diene copolymers. For simplicity and ease of description, however, the terms “propylene-based polymer” and “propylene copolymer” and “PCP” as used herein will refer to both propylene-α-olefin-diene terpolymers and propylene-diene copolymers. Such propylene-based polymers are combined with a curing agent and optional additives to form elastomeric compositions.

In at least one embodiment, the propylene-based polymer is prepared by polymerizing propylene with one or more dienes. For example, the propylene-based polymer can be prepared by polymerizing propylene with ethylene and/or at least one C₄-C₂₀ α-olefin, or a combination of ethylene and at least one C₄-C₂₀ α-olefin and one or more dienes. The one or more dienes can be conjugated or non-conjugated. Preferably, the one or more dienes are non-conjugated.

The alpha olefin comonomers can be linear or branched. Preferred linear comonomers include ethylene or C₄-C₈ α-olefins, more preferably ethylene, 1-butene, 1-hexene, and 1-octene, even more preferably ethylene or 1-butene. Preferred branched comonomers include 4-methyl-1-pentene, 3-methyl-1-pentene, and 3,5,5-trimethyl-1-hexene. In one or more embodiments, the comonomer can include styrene.

Illustrative dienes can include but are not limited to 5-ethylidene-2-norbornene (ENB); 1,4-hexadiene; 5-methylene-2-norbornene (MNB); 1,6-octadiene; 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene; 1,3-cyclopentadiene; 1,4-cyclohexadiene; vinyl norbornene (VNB); dicyclopendadiene (DCPD), and combinations thereof. Preferably, the diene is ENB.

Preferred methods and catalysts for producing the propylene-based polymers are found in publications U.S. 2004/0236042 and WO 2005/049672 and in U.S. Pat. No. 6,881,800, which are all incorporated by reference herein. Pyridine amine complexes, such as those described in WO 03/040201 are also useful to produce the propylene-based polymers useful herein. The catalyst can involve a fluxional complex, which undergoes periodic intra-molecular re-arrangement so as to provide the desired interruption of stereoregularity as in U.S. Pat. No. 6,559,262. The catalyst can be a stereorigid complex with mixed influence on propylene insertion, see Rieger EP 1070087. The catalyst described in EP 1614699 could also be used for the production of backbones suitable for the invention.

The propylene-based polymer can have an average propylene content on a weight percent basis of from about 60 wt % to about 99.7 wt %, more preferably from about 60 wt % to about 99.5 wt %, more preferably from about 60 wt % to about 97 wt %, more preferably from about 60 wt % to about 95 wt % based on the weight of the polymer. In one embodiment, the balance comprises diene. In another embodiment, the balance comprises one or more dienes and one or more of the α-olefins described previously. Other preferred ranges are from about 80 wt % to about 95 wt % propylene, more preferably from about 83 wt % to about 95 wt % propylene, more preferably from about 84 wt % to about 95 wt % propylene, and more preferably from about 84 wt % to about 94 wt % propylene based on the weight of the polymer. The balance of the propylene-based polymer comprises a diene and optionally, one or more alpha-olefins. In one or more embodiments above or elsewhere herein, the alpha-olefin is ethylene, butene, hexene, or octene. In other embodiments, two alpha-olefins are present, preferably ethylene and one of butene, hexene, or octene.

Preferably, the propylene-based polymer comprises about 0.2 wt % to about 24 wt %, of a non-conjugated diene based on the weight of the polymer, more preferably from about 0.5 wt % to about 12 wt %, more preferably about 0.6 wt % to about 8 wt %, and more preferably about 0.7 wt % to about 5 wt %. In other embodiments, the diene content ranges from about 0.2 wt % to about 10 wt %, more preferably from about 0.2 to about 5 wt %, more preferably from about 0.2 wt % to about 4 wt %, preferably from about 0.2 wt % to about 3.5 wt %, preferably from about 0.2 wt % to about 3.0 wt %, and preferably from about 0.2 wt % to about 2.5 wt % based on the weight of the polymer. In one or more embodiments above or elsewhere herein, the propylene-based polymer comprises ENB in an amount of from about 0.5 to about 4 wt %, more preferably from about 0.5 to about 2.5 wt %, and more preferably from about 0.5 to about 2.0 wt %.

In other embodiments, the propylene-based polymer preferably comprises propylene and diene in one or more of the ranges described above with the balance comprising one or more of C₂ and/or C₄-C₂₀ olefins. In general, this will amount to the propylene-based polymer preferably comprising from about 5 to about 40 wt % of one or more C₂ and/or C₄-C₂₀ olefins based the weight of the polymer. When C₂ and/or a C₄-C₂₀ olefins are present the combined amounts of these olefins in the polymer is preferably at least about 5 wt % and falling within the ranges described herein. Other preferred ranges for the one or more α-olefins include from about 5 wt % to about 35 wt %, more preferably from about 5 wt % to about 30 wt %, more preferably from about 5 wt % to about 25 wt %, more preferably from about 5 wt % to about 20 wt %, more preferably from about 5 to about 17 wt % and more preferably from about 5 wt % to about 16 wt %.

The propylene-based polymer can have a weight average molecular weight (Mw) of 5,000,000 or less, a number average molecular weight (Mn) of about 3,000,000 or less, a z-average molecular weight (Mz) of about 10,000,000 or less, and a g′ index of 0.95 or greater measured at the weight average molecular weight (Mw) of the polymer using isotactic polypropylene as the baseline, all of which can be determined by size exclusion chromatography, e.g., 3D SEC, also referred to as GPC-3D as described herein.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a Mw of about 5,000 to about 5,000,000 g/mole, more preferably a Mw of about 10,000 to about 1,000,000, more preferably a Mw of about 20,000 to about 500,000, more preferably a Mw of about 50,000 to about 400,000, wherein Mw is determined as described herein.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a Mn of about 2,500 to about 2,500,000 g/mole, more preferably a Mn of about 5,000 to about 500,000, more preferably a Mn of about 10,000 to about 250,000, more preferably a Mn of about 25,000 to about 200,000, wherein Mn is determined as described herein.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a Mz of about 10,000 to about 7,000,000 g/mole, more preferably a Mz of about 50,000 to about 1,000,000, more preferably a Mz of about 80,000 to about 700,000, more preferably a Mz of about 100,000 to about 500,000, wherein Mz is determined as described herein.

The molecular weight distribution index (MWD=(Mw/Mn)), sometimes referred to as a “polydispersity index” (PDI), of the propylene-based polymer can be about 1.5 to 40. In an embodiment the MWD can have an upper limit of 40, or 20, or 10, or 5, or 4.5, and a lower limit of 1.5, or 1.8, or 2.0. In one or more embodiments above or elsewhere herein, the MWD of the propylene-based polymer is about 1.8 to 5 and most preferably about 1.8 to 3. Techniques for determining the molecular weight (Mn and Mw) and molecular weight distribution (MWD) can be found in U.S. Pat. No. 4,540,753 (Cozewith, Ju and Ver Strate) (which is incorporated by reference herein) and references cited therein, in Macromolecules, 1988, Volume 21, pp. 3360-3371 (Ver Strate et al.), which is herein incorporated by reference for purposes of, and references cited therein, and in accordance with the procedures disclosed in U.S. Pat. No. 6,525,157, column 5, lines 1-44, which patent is hereby incorporated by reference in its entirety.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a g′ index value of 0.95 or greater, preferably at least 0.98, with at least 0.99 being more preferred, wherein g′ is measured at the Mw of the polymer using the intrinsic viscosity of isotactic polypropylene as the baseline. For use herein, the g′ index is defined as:

$g^{\prime} = \frac{\eta_{b}}{\eta_{l}}$

where η_(b) is the intrinsic viscosity of the propylene-based polymer and η₁ is the intrinsic viscosity of a linear polymer of the same viscosity-averaged molecular weight (M_(v)) as the propylene-based polymer. η₁=KM_(v) ^(α), K and α were measured values for linear polymers and should be obtained on the same instrument as the one used for the g′ index measurement.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a density of about 0.85 g/cm³ to about 0.92 g/cm³, more preferably, about 0.87 g/cm³ to 0.90 g/cm³, more preferably about 0.88 g/cm³ to about 0.89 g/cm³ at room temperature as measured per the ASTM D-1505 test method.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a melt flow rate (MFR, 2.16 kg weight @ 230° C.), equal to or greater than 0.2 g/10 min as measured according to the ASTM D-1238(A) test method as modified (described below). Preferably, the MFR (2.16 kg @ 230° C.) is from about 0.5 g/10 min to about 200 g/10 min and more preferably from about 1 g/10 min to about 100 g/10 min. In an embodiment, the propylene-based polymer has an MFR of 0.5 g/10 min to 200 g/10 min, especially from 2 g/10 min to 30 g/10 min, more preferably from 5 g/10 min to 30 g/10 min, more preferably 10 g/10 min to 30 g/10 min, more preferably 10 g/10 min to about 25 g/10 min, or more preferably 2 g/10 min to about 10 g/10 min.

The propylene-based polymer can have a Mooney viscosity ML (1+4)@125° C., as determined according to ASTM D1646, of less than 100, more preferably less than 75, even more preferably less than 60, most preferably less than 30.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can have a heat of fusion (Hf) measured by Differential Scanning Calorimetry (DSC), which is greater than or equal to about 0.5 Joules per gram (J/g), and is ≦about 80 J/g, preferably ≦about 75 J/g, preferably ≦about 70 J/g, more preferably ≦about 60 J/g, more preferably ≦about 50 J/g, more preferably ≦about 35 J/g. Also preferably, the propylene-based polymer has a heat of fusion that is greater than or equal to about 1 J/g, preferably greater than or equal to about 5 J/g. In another embodiment, the propylene-based polymer can have a heat of fusion (Hf), which is from about 0.5 J/g to about 75 J/g, preferably from about 1 J/g to about 75 J/g, more preferably from about 0.5 J/g to about 35 J/g. Preferred propylene-based polymers and compositions can be characterized in terms of both their melting points (Tm) and heats of fusion, which properties can be influenced by the presence of comonomers or steric irregularities that hinder the formation of crystallites by the polymer chains. In one or more embodiments, the heat of fusion ranges from a lower limit of 1.0 J/g, or 1.5 J/g, or 3.0 J/g, or 4.0 J/g, or 6.0 J/g, or 7.0 J/g, to an upper limit of 30 J/g, or 35 J/g, or 40 J/g, or 50 J/g, or 60 J/g or 70 J/g, or 75 J/g, or 80 J/g.

The crystallinity of the propylene-based polymer can also be expressed in terms of percentage of crystallinity (i.e., % crystallinity). In one or more embodiments above or elsewhere herein, the propylene-based polymer has a % crystallinity of from 0.5% to 40%, preferably 1% to 30%, more preferably 5% to 25% wherein % crystallinity is determined by DSC. In another embodiment, the propylene-based polymer preferably has a crystallinity of less than 40%, preferably about 0.25% to about 25%, more preferably from about 0.5% to about 22%, and most preferably from about 0.5% to about 20%. As disclosed above, the thermal energy for the highest order of polypropylene is estimated at 189 J/g (i.e., 100% crystallinity is equal to 209 J/g).

In addition to this level of crystallinity, the propylene-based polymer preferably has a single broad melting transition. However, the propylene-based polymer can show secondary melting peaks adjacent to the principal peak, but for purposes herein, such secondary melting peaks are considered together as a single melting point, with the highest of these peaks (relative to baseline as described herein) being considered the melting point of the propylene-based polymer.

The propylene-based polymer preferably has a melting point (measured by DSC) of equal to or less than 100° C., preferably less than 90° C., preferably less than 80° C., more preferably less than or equal to 75° C., preferably from about 25° C. to about 80° C., preferably about 25° C. to about 75° C., more preferably about 30° C. to about 65° C.

Differential Scanning Calorimetry, or DSC, is used to determine heat of fusion and melting temperature of the propylene-based polymer. The method is as follows: about 0.5 grams of polymer is weighed out and pressed to a thickness of about 15-20 mils (about 381-508 microns) at about 140° C.-150° C., using a “DSC mold” and Mylar as a backing sheet. The pressed pad is allowed to cool to ambient temperature by hanging in air (the Mylar is not removed). The pressed pad is annealed at room temperature (23° C.-25° C.) for about 8 days. At the end of this period, an about 15-20 mg disc is removed from the pressed pad using a punch die and is placed in a 10 microliter aluminum sample pan. The sample is placed in a Differential Scanning Calorimeter (Perkin Elmer Pyris 1 Thermal Analysis System) and is cooled to about −100° C. The sample is heated at 10° C./min to attain a final temperature of about 165° C. The thermal output, recorded as the area under the melting peak of the sample, is a measure of the heat of fusion and can be expressed in Joules per gram of polymer and is automatically calculated by the Perkin Elmer System. The melting point is recorded as the temperature of the greatest heat absorption within the range of melting of the sample relative to a baseline measurement for the increasing heat capacity of the polymer as a function of temperature.

The propylene-based polymer can have a triad tacticity of three propylene units, as measured by ¹³C NMR of 75% or greater, 80% or greater, 82% or greater, 85% or greater, or 90% or greater. Preferred ranges include from about 50 to about 99%, more preferably from about 60 to about 99%, more preferably from about 75 to about 99% and more preferably from about 80 to about 99%; and in other embodiments from about 60 to about 97%. Triad tacticity is determined by the methods described in U.S. Patent Application Publication No. 2004/0236042.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can be a blend of discrete random propylene-based polymers. Such blends can include ethylene-based polymers and propylene-based polymers, or at least one of each such ethylene-based polymers and propylene-based polymers. The number of propylene-based polymers can be three or less, more preferably two or less.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can include a blend of two propylene-based polymers differing in the olefin content, the diene content, or both.

In one or more embodiments above or elsewhere herein, the propylene-based polymer can include a propylene based elastomeric polymer produced by random polymerization processes leading to polymers having randomly distributed irregularities in stereoregular propylene propagation. This is in contrast to block copolymers in which constituent parts of the same polymer chains are separately and sequentially polymerized.

In another embodiment, the propylene-based polymers can include copolymers prepared according the procedures in WO 02/36651. Likewise, the propylene-based polymer can include polymers consistent with those described in WO 03/040201, WO 03/040202, WO 03/040095, WO 03/040201, WO 03/040233, and/or WO 03/040442. Additionally, the propylene-based polymer can include polymers consistent with those described in EP 1233191, and U.S. Pat. No. 6,525,157, along with suitable propylene homo- and copolymers described in U.S. Pat. No. 6,770,713 and U.S. Patent Application Publication No. 2005/215964, all of which are incorporated by reference. The propylene-based polymer can also include one or more polymers consistent with those described in EP 1614699 or EP 1017729.

Grafted (Functionalized) Backbone

In one or more embodiments, the propylene-based polymer can be grafted (i.e. “functionalized”) using one or more grafting monomers. As used herein, the term “grafting” denotes covalent bonding of the grafting monomer to a polymer chain of the propylene-based polymer. The grafting monomer can be or include at least one hydrolysable silane component. A preferred hydrolysable silane component can be or include vinyl siloxane. Preferred vinyl siloxanes include vinyl triethoxysilane and vinyl trimethoxysilane.

In one or more embodiments, the grafting monomer can be or include at least one organic silane having the general formula YSiRR″₂, wherein Y is selected from vinyl terminated radicals, each R″ is independently selected from one or more hydrolysable organic radicals; and R can be a Y radical, a R″ radical, or selected from C₁-C₁₀ alkyl radicals (both R and R″ are bound to the silicon atom). In a particular embodiment, Y is selected from a vinyl radical, vinyl terminated C₁-C₁₀ alkyl radicals, vinyl terminated C₁-C₁₀ alkoxy radicals, and vinyl terminated C₁-C₁₀ alkoxy radicals. The vinyl terminated radical is preferably selected from vinyl, allyl, butenyl, cyclohexenyl, cyclopentadienyl, and cyclohexadienyl radicals.

In one or more embodiments, the grafting monomer can be or include one or more ethylenically unsaturated carboxylic acid or acid derivatives, such as an acid anhydride, ester, salt, amide, imide, acrylates or the like. Illustrative monomers include but are not limited to: acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, mesaconic acid, maleic anhydride, 4-methyl cyclohexene-1,2-dicarboxylic acid anhydride, bicyclo(2.2.2)octene-2,3-dicarboxylic acid anhydride, 1,2,3,4,5,8,9,10-octahydronaphthalene-2,3-dicarboxylic acid anhydride, 2-oxa-1,3-diketospiro (4.4)nonene, bicyclo(2.2.1)heptene-2,3-dicarboxylic acid anhydride, maleopimaric acid, tetrahydrophthalic anhydride, norbornene-2,3-dicarboxylic acid anhydride, nadic anhydride, methyl nadic anhydride, himic anhydride, methyl himic anhydride, and 5-methylbicyclo(2.2.1)heptene-2,3-dicarboxylic acid anhydride. Other suitable grafting monomers include methyl acrylate and higher alkyl acrylates, methyl methacrylate and higher alkyl methacrylates, acrylic acid, methacrylic acid, hydroxy-methyl methacrylate, hydroxyl-ethyl methacrylate and higher hydroxy-alkyl methacrylates and glycidyl methacrylate. Maleic anhydride is a preferred grafting monomer.

In one or more embodiments, the grafted propylene-based polymer comprises of from about 0.5 to about 10 wt % grafting monomer, more preferably from about 0.5 to about 6 wt %, more preferably from about 0.5 to about 3 wt %; in other embodiments from about 1 to about 6 wt %, more preferably from about 1 to about 3 wt %, based on the weight of the propylene-α-olefin. In a preferred embodiment, the grafting monomer concentration in the grafted polymer ranges from about 1 wt % to about 6 wt %, from about 1.5 wt % to about 6 wt %, from about 1.8 wt % to about 5.5 wt %, or from about 2.0 wt % to about 5.3 wt %.

Free Radical Initiator

In one or more embodiments, a free radical generating catalyst or initiator can be used to initiate the graft polymerization reaction. Illustrative initiators include but are not limited to: diacyl peroxides such as benzoyl peroxide; peroxyesters such as tert-butylperoxy benzoate, tert-butylperoxy acetate, OO-tert-butyl-O-(2-ethylhexyl)monoperoxy carbonate; peroxyketals such as n-butyl-4,4-di-(tert-butyl peroxy)valerate; and dialkyl peroxides such as 1,1-bis(tertbutylperoxy)cyclohexane, 1,1-bis(tert-butylperoxy)-3,3,5-trimethylcyclohexane, 2,2-bis(tert-butylperoxy)butane, dicumylperoxide, tert-butylcumylperoxide, di-(2-tert-butylperoxy-isopropyl-(2))benzene, di-tert-butylperoxide (DTBP), 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexyne, 3,3,5,7,7-pentamethyl 1,2,4-trioxepane; and the like. Most preferred free-radical initiators are organic peroxides such as benzoyl peroxide, dichlorobenzoyl peroxide, dicumyl peroxide, di-tertiary butyl peroxide. The most preferred free-radical initiator is dicumyl peroxide. Other suitable free-radical initiators are described in U.S. Pat. No. 3,646,155.

The free-radical initiator can be added at the same time as the grafting monomer, or after addition of the grafting monomer. The preferred sequence for the grafting reaction melts the propylene-based polymer, adds and disperses the grafting monomer, introduces the initiator and vents the unreacted monomer and by-products resulting from the initiator decomposition. Other sequences can feed the monomers and the initiator pre-dissolved in a solvent. Preferably, the free-radical initiator is added in an amount of from 0.1 to 1.0 wt % of the propylene-α-olefin, more preferably from 0.05 to 0.2 wt %. In one or more embodiments, the initiator concentration in the grafted polymer ranges from about 0.01 wt % to about 4 wt %, from about 0.5 wt % to about 3.8 wt %, from about 1.0 wt % to about 3.3 wt %, or from about 0.1 wt % to about 2.0 wt %.

Polyolefinic Thermoplastic Resin

The term “polyolefinic thermoplastic resin” as used herein refers to any material that is not a “rubber” and that is a polymer or polymer blend having a melting point of 70° C. or more and considered by persons skilled in the art as being thermoplastic in nature, e.g., a polymer that softens when exposed to heat and returns to its original condition when cooled to room temperature. The polyolefinic thermoplastic resin can contain one or more polyolefins, including polyolefin homopolymers and polyolefin copolymers. Except as stated otherwise, the term “copolymer” means a polymer derived from two or more monomers (including terpolymers, tetrapolymers, etc.), and the term “polymer” refers to any carbon-containing compound having repeat units from one or more different monomers.

Illustrative polyolefins can be prepared from mono-olefin monomers including, but are not limited to, monomers having 2 to 7 carbon atoms, such as ethylene, propylene, 1-butene, isobutylene, 1-pentene, 1-hexene, 1-octene, 3-methyl-1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene, mixtures thereof and copolymers thereof with (meth)acrylates and/or vinyl acetates. Preferably, the polyolefinic thermoplastic resin component is unvulcanized or non crosslinked.

In one or more embodiments, the polyolefinic thermoplastic resin contains polypropylene. The term “polypropylene” as used herein broadly means any polymer that is considered a “polypropylene” by persons skilled in the art (as reflected in at least one patent or publication), and includes homo, impact, and random polymers of propylene. Preferably, the polypropylene used in the compositions described herein has a melting point above 110° C., includes at least 90 wt % propylene units, and contains isotactic sequences of those units. The polypropylene can also include atactic sequences or s syndiotactic sequences, or both. The polypropylene can also include essentially syndiotactic sequences such that the melting point of the polypropylene is above 110° C. The polypropylene can either derive exclusively from propylene monomers (i.e., having only propylene units) or derive from mainly propylene (more than 80% propylene) with the remainder derived from olefins, particularly ethylene, and/or C₄-C₁₀ α-olefins. As noted elsewhere herein, certain polypropylenes have a high MFR (e.g., from a low of 10, or 15, or 20 g/10 min to a high of 25 to 30 g/10 min. Others have a lower MFR, e.g., “fractional” polypropylenes which have an MFR less than 1.0. Those with high MFR can be preferred for ease of processing or compounding.

In one or more embodiments, the polyolefinic thermoplastic resin is or includes isotactic polypropylene. Preferably, the polyolefinic thermoplastic resin contains one or more crystalline propylene homopolymers or copolymers of propylene having a melting temperature greater than 105° C. as measured by DSC. Preferred copolymers of propylene include, but are not limited to, terpolymers of propylene, impact copolymers of propylene, random polypropylene and mixtures thereof. Preferred comonomers have 2 carbon atoms, or from 4 to 12 carbon atoms. Preferably, the comonomer is ethylene. Such polyolefinic thermoplastic resin and methods for making the same are described in U.S. Pat. No. 6,342,565.

The term “random polypropylene” as used herein broadly means a copolymer of propylene having up to 9 wt %, preferably 2 wt % to 8 wt % of an alpha olefin comonomer. Preferred alpha olefin comonomers have 2 carbon atoms, or from 4 to 12 carbon atoms. Preferably, the alpha olefin comonomer is ethylene.

In one or more embodiments, the random polypropylene has a 1% secant modulus of about 100 kPsi to about 200 kPsi, as measured according to ASTM D790A. In one or more embodiments, the 1% secant modulus can be 140 kPsi to 170 kPsi, as measured according to ASTM D790A. In one or more embodiments, the 1% secant modulus can be 140 kPsi to 160 kPsi, as measured according to ASTM D790A. In one or more embodiments, the 1% secant modulus can range from a low of about 100, 110, or 125 kPsi to a high of about 145, 160, or 175 kPsi, as measured according to ASTM D790A.

In one or more embodiments, the random polypropylene can have a density of about 0.85 to about 0.95 g/cc, as measured by ASTM D792. In one or more embodiments, the random polypropylene can have a density of about 0.89 g/cc to 0.92 g/cc, as measured by ASTM D792. In one or more embodiments, the density can range from a low of about 0.85, 0.87, or 0.89 g/cc to a high of about 0.90, 0.91, 0.92 g/cc, as measured by ASTM D792.

Secondary Elastomeric Component

The elastomeric composition can optionally include one or more secondary elastomeric components. In at least one specific embodiment, the secondary elastomeric component can be or include one or more ethylene-propylene copolymers (EP). Preferably, the ethylene-propylene polymer (EP) is non-crystalline, e.g., atactic or amorphous, but in certain embodiments the EP may be crystalline (including “semi-crystalline”). The crystallinity of the EP is preferably derived from the ethylene, and a number of published methods, procedures and techniques are available for evaluating whether the crystallinity of a particular material is derived from ethylene. The crystallinity of the EP can be distinguished from the crystallinity of the propylene-based polymer by removing the EP from the composition and then measuring the crystallinity of the residual propylene-based polymer. Such crystallinity measured is usually calibrated using the crystallinity of polyethylene and related to the comonomer content. The percent crystallinity in such cases is measured as a percentage of polyethylene crystallinity and thus the origin of the crystallinity from ethylene is established.

In one or more embodiments, the EP can include one or more optional polyenes, including particularly a diene; thus, the EP can be an ethylene-propylene-diene (commonly called “EPDM”). The optional polyene is considered to be any hydrocarbon structure having at least two unsaturated bonds wherein at least one of the unsaturated bonds is readily incorporated into a polymer. The second bond may partially take part in polymerization to form long chain branches but preferably provides at least some unsaturated bonds suitable for subsequent curing or vulcanization in post polymerization processes. Examples of EP or EPDM copolymers include V722, V3708P, MDV 91-9, V878 that are available under the trade name Vistalon from ExxonMobil Chemicals. Several commercial EPDM are available from DOW under the trade Nordel IP amd MG grades.). Certain rubber components (e.g., EPDMs, such as Vistalon 3666) include additive oil that is preblended before the rubber component is combined with the thermoplastic. The type of additive oil utilized will be that customarily used in conjunction with a particular rubber component.

Examples of the optional polyene include, but are not limited to, butadiene, pentadiene, hexadiene (e.g., 1,4-hexadiene), heptadiene (e.g., 1,6-heptadiene), octadiene (e.g., 1,7-octadiene), nonadiene (e.g., 1,8-nonadiene), decadiene (e.g., 1,9-decadiene), undecadiene (e.g., 1,10-undecadiene), dodecadiene (e.g., 1,11-dodecadiene), tridecadiene (e.g., 1,12-tridecadiene), tetradecadiene (e.g., 1,13-tetradecadiene), pentadecadiene, hexadecadiene, heptadecadiene, octadecadiene, nonadecadiene, icosadiene, heneicosadiene, docosadiene, tricosadiene, tetracosadiene, pentacosadiene, hexacosadiene, heptacosadiene, octacosadiene, nonacosadiene, triacontadiene, and polybutadienes having a molecular weight (Mw) of less than 1000 g/mol. Examples of straight chain acyclic dienes include, but are not limited to 1,4-hexadiene and 1,6-octadiene. Examples of branched chain acyclic dienes include, but are not limited to 5-methyl-1,4-hexadiene, 3,7-dimethyl-1,6-octadiene, and 3,7-dimethyl-1,7-octadiene. Examples of single ring alicyclic dienes include, but are not limited to 1,4-cyclohexadiene, 1,5-cyclooctadiene, and 1,7-cyclododecadiene. Examples of multi-ring alicyclic fused and bridged ring dienes include, but are not limited to tetrahydroindene; norbornadiene; methyltetrahydroindene; dicyclopentadiene; bicyclo(2.2.1)hepta-2,5-diene; and alkenyl-, alkylidene-, cycloalkenyl-, and cylcoalkyliene norbornenes [including, e.g., 5-methylene-2-norbornene, 5-ethylidene-2-norbornene, 5-propenyl-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene, 5-cyclohexylidene-2-norbornene, and 5-vinyl-2-norbornene]. Examples of cycloalkenyl-substituted alkenes include, but are not limited to vinyl cyclohexene, allyl cyclohexene, vinylcyclooctene, 4-vinylcyclohexene, allyl cyclodecene, vinylcyclododecene, and tetracyclododecadiene.

In another embodiment, the secondary elastomeric component can include, but is not limited to, styrene/butadiene rubber (SBR), styrene/isoprene rubber (SIR), styrene/isoprene/butadiene rubber (SIBR), styrene-butadiene-styrene block copolymer (SBS), hydrogenated styrene-butadiene-styrene block copolymer (SEBS), hydrogenated styrene-butadiene block copolymer (SEB), styrene-isoprene-styrene block copolymer (SIS), styrene-isoprene block copolymer (SI), hydrogenated styrene-isoprene block copolymer (SEP), hydrogenated styrene-isoprene-styrene block copolymer (SEPS), styrene-ethylene/butylene-ethylene block copolymer (SEBE), styrene-ethylene-styrene block copolymer (SES), ethylene-ethylene/butylene block copolymer (EEB), ethylene-ethylene/butylene/styrene block copolymer (hydrogenated BR-SBR block copolymer), styrene-ethylene/butylene-ethylene block copolymer (SEBE), ethylene-ethylene/butylene-ethylene block copolymer (EEBE), polyisoprene rubber, polybutadiene rubber, isoprene butadiene rubber (IBR), polysulfide, nitrile rubber, propylene oxide polymers, star-branched butyl rubber and halogenated star-branched butyl rubber, brominated butyl rubber, chlorinated butyl rubber, star-branched polyisobutylene rubber, star-branched brominated butyl (polyisobutylene/isoprene copolymer) rubber; poly(isobutylene-co-alkylstyrene), preferably isobutylene/methylstyrene copolymers such as isobutylene/meta-bromomethylstyrene, isobutylene/bromomethylstyrene, isobutylene/chloromethylstyrene, halogenated isobutylene cyclopentadiene, and isobutylene/chloromethylstyrene and mixtures thereof. Preferred secondary elastomeric components include hydrogenated styrene-butadiene-styrene block copolymer (SEBS), and hydrogenated styrene-isoprene-styrene block copolymer (SEPS).

The secondary elastomeric component can also be or include natural rubber. Natural rubbers are described in detail by Subramaniam in RUBBER TECHNOLOGY pp. 179-208 (1995). Suitable natural rubbers can be selected from the group consisting of Malaysian rubber such as SMR CV, SMR 5, SMR 10, SMR 20, and SMR 50 and mixtures thereof, wherein the natural rubbers have a Mooney viscosity at 100° C. (ML 1+4) of from 30 to 120, more preferably from 40 to 65. The Mooney viscosity test referred to herein is in accordance with ASTM D-1646.

The secondary elastomeric component can also be or include one or more synthetic rubbers. One suitable commercially available synthetic rubber include NATSYN™ (Goodyear Chemical Company), and BUDENE™ 1207 or BR 1207 (Goodyear Chemical Company). A desirable rubber is high cis-polybutadiene (cis-BR). By “cis-polybutadiene” or “high cis-polybutadiene”, it is meant that 1,4-cis polybutadiene is used, wherein the amount of cis component is at least 95%. An example of high cis-polybutadiene commercial products used in the composition BUDENE™ 1207.

The secondary elastomeric component can be present in a range from up to 50 phr in one embodiment, from up to 40 phr in another embodiment, and from up to 30 phr in yet another embodiment. In one or more embodiments, the amount of the secondary rubber component can range from a low of about 1, 7, or 20 phr to a high of about 25, 35, or 50 phr.

Additive Oil

The elastomeric composition can optionally include one or more additive oils. The term “additive oil” includes both “process oils” and “extender oils.” For example, “additive oil” may include hydrocarbon oils and plasticizers, such as organic esters and synthetic plasticizers. Many additive oils are derived from petroleum fractions, and have particular ASTM designations depending on whether they fall into the class of paraffinic, naphthenic, or aromatic oils. Other types of additive oils include mineral oil, alpha olefinic synthetic oils, such as liquid polybutylene, e.g., products sold under the trademark Parapol®. Additive oils other than petroleum based oils can also be used, such as oils derived from coal tar and pine tar, as well as synthetic oils, e.g., polyolefin materials (e.g., SpectaSyn™ and Elevast™, both supplied by ExxonMobil Chemical Company.

The ordinarily skilled chemist will recognize which type of oil should be used with a particular rubber, and also be able to determine the amount (quantity) of oil. The additive oil can be present in amounts from about 5 to about 300 parts by weight per 100 parts by weight of the blend of the rubber and thermoplastic components. The amount of additive oil may also be expressed as from about 30 to 250 parts, and more desirably from about 70 to 200 parts by weight per 100 parts by weight of the rubber component. Alternatively, the quantity of additive oil can be based on the total rubber content, and defined as the ratio, by weight, of additive oil to total rubber and that amount may in certain cases be the combined amount of process oil and extender oil. The ratio may range, for example, from about 0 to about 4.0/1. Other ranges, having any of the following lower and upper limits, may also be utilized: a lower limit of 0.1/1, or 0.6/1, or 0.8/1, or 1.0/1, or 1.2/1, or 1.5/1, or 1.8/1, or 2.0/1, or 2.5/1; and an upper limit (which may be combined with any of the foregoing lower limits) of 4.0/1, or 3.8/1, or 3.5/1, or 3.2/1, or 3.0/1, or 2.8/1. Larger amounts of additive oil can be used, although the deficit is often reduced physical strength of the composition, or oil weeping, or both.

Polybutene oils are preferred. Preferable polybutene oils have an Mn of less than 15,000, and include homopolymer or copolymer of olefin derived units having from 3 to 8 carbon atoms and more preferably from 4 to 6 carbon atoms. In one or more embodiments, the polybutene is a homopolymer or copolymer of a C₄ raffinate. An embodiment of preferred low molecular weight polymers termed “polybutene” polymers is described in, for example, SYNTHETIC LUBRICANTS AND HIGH-PERFORMANCE FUNCTIONAL FLUIDS pp. 357-392 (Leslie R. Rudnick & Ronald L. Shubkin, ed., Marcel Dekker 1999) (hereinafter “polybutene processing oil” or “polybutene”).

In one or more embodiments, the polybutene processing oil is a copolymer having at least isobutylene derived units, and optionally 1-butene derived units, and/or 2-butene derived units. In one embodiment, the polybutene is a homopolymer if isobutylene, or a copolymer of isobutylene and 1-butene or 2-butene, or a terpolymer of isobutylene and 1-butene and 2-butene, wherein the isobutylene derived units are from 40 to 100 wt % of the copolymer, the 1-butene derived units are from 0 to 40 wt % of the copolymer, and the 2-butene derived units are from 0 to 40 wt % of the copolymer. In another embodiment, the polybutene is a copolymer or terpolymer wherein the isobutylene derived units are from 40 to 99 wt % of the copolymer, the 1-butene derived units are from 2 to 40 wt % of the copolymer, and the 2-butene derived units are from 0 to 30 wt % of the copolymer. In yet another embodiment, the polybutene is a terpolymer of the three units, wherein the isobutylene derived units are from 40 to 96 wt % of the copolymer, the 1-butene derived units are from 2 to 40 wt % of the copolymer, and the 2-butene derived units are from 2 to 20 wt % of the copolymer. In yet another embodiment, the polybutene is a homopolymer or copolymer of isobutylene and 1-butene, wherein the isobutylene derived units are from 65 to 100 wt % of the homopolymer or copolymer, and the 1-butene derived units are from 0 to 35 wt % of the copolymer. Commercial examples of a suitable processing oil includes the PARAPOL™ Series of processing oils or Polybutene grades or Indopol™ from Soltex Synthetic Oils and Lubricants or from BP/Innovene.

The processing oil or oils can be present at 1 to 60 phr in one embodiment, and from 2 to 40 phr in another embodiment, from 4 to 35 phr in another embodiment, and from 5 to 30 phr in yet another embodiment.

Co-Agents

The elastomeric composition can optionally include one or more co-agents. Suitable co-agents can include liquid and metallic multifunctional acrylates and methacrylates, functionalized polybutadiene resins, functionalized cyanurate, and allyl isocyanurate. More particularly, suitable co-agents can include, but are not limited to polyfunctional vinyl or allyl compounds such as, for example, triallyl cyanurate, triallyl isocyanurate, trimethylolpropane trimethacrylate, pentaerthritol tetramethacrylate, ethylene glycol dimethacrylate, diallyl maleate, dipropargyl maleate, dipropargyl monoallyl cyanurate, azobisisobutyronitrile and the like, and combinations thereof. Commercially available co-agents can be purchased from Sartomer.

In one or more embodiments, the elastomeric composition contains at least 0.1 wt % of co-agent based on the total weight of blend. In one or more embodiments, the amount of co-agent(s) can range from about 0.1 wt % to about 15 wt %, based on the total weight of blend. In one or more embodiments, the amount of co-agent(s) can range from a low of about 0.1 wt %, 1.5 wt % or 3.0 wt % to a high of about 4.0 wt %, 7.0 wt %, or 15 wt %, based on the total weight of blend. In one or more embodiments, the amount of co-agent(s) can range from a low of about 2.0 wt %, 3.0 wt % or 5.0 wt % to a high of about 7.0 wt %, 9.5 wt %, or 12.5 wt %, based on the total weight of blend. In one or more embodiments, the amount of co-agent(s) is about 3 wt %, based on the total weight of blend.

Antioxidants

The elastomeric composition can optionally include one or more anti-oxidants. Suitable anti-oxidants can include hindered phenols, phosphites, hindered amines, Irgafos 168, Irganox 1010, Irganox 3790, Irganox B225, Irganxo 1035, Irgafos 126, Irgastab 410, Chimassorb 944, etc. made by Ciba Geigy Corp. These may be added to the elastomeric composition to protect against degradation during shaping or fabrication operation and/or to better control the extent of chain degradation.

In one or more embodiments, the elastomeric composition contains at least 0.1 wt % of antioxidant, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) can range from about 0.1 wt % to about 5 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) can range from a low of about 0.1 wt %, 0.2 wt % or 0.3 wt % to a high of about 1 wt %, 2.5 wt %, or 5 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) is about 0.1 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) is about 0.2 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) is about 0.3 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) is about 0.4 wt %, based on the total weight of blend. In one or more embodiments, the amount of antioxidant(s) is about 0.5 wt %, based on the total weight of blend.

Blending and Additives

In one or more embodiments, the individual materials and components, such as the propylene-based polymer, grafting monomer, free radical initiator, and optionally the one or more polyolefinic thermoplastic resins, secondary elastomeric component, additive oil, co-agents, and anti-oxidants can be blended by melt-mixing to form a blend. Examples of machinery capable of generating the shear and mixing include extruders with kneaders or mixing elements with one or more mixing tips or flights, extruders with one or more screws, extruders of co or counter rotating type, Banbury mixer, Farrell Continuous mixer, and the Buss Kneader. The type and intensity of mixing, temperature, and residence time required can be achieved by the choice of one of the above machines in combination with the selection of kneading or mixing elements, screw design, and screw speed (<3000 RPM).

In one or more embodiments, the blend can include the propylene-based polymer in an amount ranging from a low of about 51 wt %, 60 wt %, 70 wt %, or 75 wt % to a high of about 80 wt %, 90 wt %, 95 wt %, or 99 wt %. In one or more embodiments, the blend can include the one or more polyolefinic thermoplastic components in an amount ranging from a low of about 5 wt %, 10 wt %, or 20 wt % to a high of about 25 wt %, 30 wt %, or 40 wt %. In one or more embodiments, the blend can include the secondary elastomeric component in an amount ranging from a low of about 5 wt %, 10 wt %, or 15 wt % to a high of about 20 wt %, 35 wt %, or 40 wt %. In one or more embodiments, the blend can include the one or more additives, co-agents, and/or anti-oxidants in an amount ranging from a low of about 0.001 wt %, 0.01 wt %, or 0.1 wt % to a high of about 0.5 wt %, 1.0 wt %, 2.5 wt %, or 5.0 wt %. Unless otherwise noted herein, all weight percents (wt %) are based on the total weight of the blended composition.

In one or more embodiments, the co-agents, antioxidants, and/or other additives can be introduced at the same time as the other polymer components or later downstream in case of using an extruder or Buss kneader or only later in time. In addition to the co-agents and antioxidants described, other additives can include antiblocking agents, antistatic agents, ultraviolet stabilizers, foaming agents, and processing aids. The additives can be added to the blend in pure form or in master batches.

Conventional propylene-based polymers are disclosed, for example, in U.S. Pat. Nos. 6,525,157, 6,500,563, and 6,342,565, each of which is herein incorporated by reference in its entirety. U.S. Pat. No. 6,342,565, in particular, discloses a soft, set-resistant, annealed fiber comprising a blend of polyolefins. Other conventional compositions are described in WO 04/014988, WO 03/040233, WO 00/69963, EP 0946640, EP 0964641, EP 969043, and EP 1098934, each of which is herein incorporated by reference in its entirety. EP 1003814 and U.S. Pat. No. 6,642,316, each of which is herein incorporated by reference in its entirety, disclose two-component blends of small amounts of isotactic polypropylene and an ethylene based elastomer. EP 0374695 discloses two component blends using 40 wt % or less of the propylene-based copolymer. EP 0510559 A2, WO 2005/003199, U.S. Pat. Nos. 6,472,015, 6,455,637, 5,844,009, 5,883,145, and U.S. Patent Application Publication Nos. 2002/0151647 and 2003/0050401, each of which is herein incorporated by reference in its entirety, disclose grafted polyethylene-based compositions having at least 50 wt % ethylene derived units.

One problem with using polyethylene-based polymers in forming graft polymers is that the peroxides that are used to initiate the grafting also act as a cross-linking agent towards polyethylene. Thus, what results from contacting peroxides with polyethylene-based polymers is a highly cross-linked polymer with higher molecular weight, and high viscosity, which is even worse when high silane levels, which necessitate the use of high levels of peroxides, are required to get higher performance. Such compositions are not suitable for stretchable application as they lack stretchability at room and elevated temperatures due to its crystalline nature.

The article S. Yang et al., “Mechanism of a One-Step Method for Preparing Silane Grafting and Cross-linking Polypropylene” in Volume 47, Issue 7, POLYMER ENGINEERING AND SCIENCE, pp. 1004-1008 (2007), which is incorporated herein by reference, discloses the grafting of silane to polypropylene, thus forming moisture cross-linkable propylene homopolymer. Other related references include U.S. Pat. No. 3,646,155 and U.S. Patent Publication Nos. 2006/0102149, 2005/0107529, 2005/0107530, 2005/0131142, and 2005/0107534, each of which are incorporated herein by reference.

Preparing Grafted Propylene-Based Polymers

The grafted propylene-based polymer can be prepared using conventional techniques. For example, the graft polymer can be prepared in solution, in a fluidized bed reactor, or by melt grafting. A preferred grafted polymer can be prepared by melt blending in a shear-imparting reactor, such as an extruder reactor. Single screw but preferably twin screw extruder reactors such as co-rotating intermeshing extruder or counter-rotating non-intermeshing extruders but also co-kneaders such as those sold by Buss are especially preferred.

In at least one specific embodiment, the propylene-based polymer, grafting monomer, free-radical initiator, and optionally one or more polyolefinic thermoplastic resins, and optionally one or more elastomers can be reacted at a temperature above the melting point of the propylene-based polymer under conditions at which the propylene-based polymer is subjected to mechanical shearing, using processes known to those skilled in the art. The grafted propylene-based polymer can be subsequently melt-processed (such as by a Brabender or single or double screw extruder that can apply a shearing force on the molten material), in one embodiment with an amount of one or more condensation catalysts that facilitate the cross-linking reaction of the grafted copolymer after fabricating into articles of use. The condensation catalyst (or “catalyst”) can be selected from the group consisting of organic bases, carboxylic acids and organometallic compounds including organic titanates and complexes or carboxylates of lead, cobalt, iron, nickel, zinc and tin. Preferably, the catalyst is selected from dibutyltin dilaurate, dibutyltin diacetate, dibutyltin octanoate, dioctyltin maleate, dibutyltin oxide and titanium compounds such as titanium-2-ethylhexoxide. A preferred condensation catalyst includes dibutyl tindilaurate, though any material that will catalyze the condensation reaction is suitable. The condensation catalyst is preferably added in an amount of from 0.01 to 5 wt %, and from 0.01 to 3 wt % in another embodiment, more preferably 0.05 to 2 wt %, and most preferably 0.1 to 1 wt % (by weight of the grafted propylene-based polymer). In one or more embodiments, the amount of condensation catalyst ranges from about 0.01 wt % to about 5 wt %, from about 0.5 wt % to about 4.2 wt %, from about 1.0 wt % to about 3.3 wt %, or from about 0.1 wt % to about 2.0 wt %, based on total weight of the blend composition.

Subjecting the composition thus produced to moisture, at an elevated temperature of greater than about 20° C., or greater than about 30° C., or greater than about 40° C. or greater than about 50° C., preferably of from 20° C. to 85° C., will induce crosslinking of the silane groups via a combined hydrolysis and condensation reaction. Atmospheric moisture is usually sufficient to permit the crosslinking to occur, but the rate of crosslinking may be increased by the use of an artificially moistened atmosphere, or by immersion in liquid water. For example, crosslinking is induced by a relative humidity of at least about 50%, or at least about 60%, or at least about 75% for at least about 10 hours, or at least about 25 hours, or at least about 50 hours, or at least about 75 hours. Preferably crosslinking is induced by exposure to at least about 90% relative humidity for approximately 100 hours. Also, subjecting the composition to heat and moisture will accelerate the crosslinking reaction. Most preferably, crosslinking is effected at a temperature of at least about 50° C. and most preferably by exposing the composition to a temperature of about 85° C. and a relative humidity of about 90% for approximately 100 hours. The end result is a cross-linked propylene-based polymer (or “cross-linked copolymer blend”).

In at least one other specific embodiment, the propylene-based polymer, grafting monomer, free-radical initiator, and condensation catalyst, and optional polyolefinic thermoplastic resins, elastomers, and/or additives, can be pre-blended and passed through an extruder at a temperature above the melting point of the propylene-based polymer and decomposition temperature of the peroxide, in order to graft the silane onto the propylene-based polymer. Thus is produced the grafted propylene-based polymer (or copolymer blend composition). The grafted polymer can then be passed through a multi-strand die, cooled, and subsequently chopped into pellets with a strand pelletizer and dried. The pellets can then be melted and fabricated into a formed article that can be exposed to moisture at any time, preferably at a temperature above about 50° C. and most preferably by exposing the composition to a temperature of about 85° C. and a relative humidity of about 90% for approximately 100 hours, to effect crosslinking of the material.

Cured Products

Formed articles include extruded articles, such as pellets, fibers, yarns, or films, and articles made therefrom, such as coatings, nonwoven fabrics, and woven fabrics. Preferably the articles are at least partially crosslinked or cured. Preferably, the formed article is at least partially crosslinked or cured so that the article becomes heat-resistant. As used herein, the term “heat-resistant” refers to the ability of a polymer composition or an article formed from a polymer composition to pass the high temperature heat-setting and dyeing tests described herein. As used herein, the terms “cured,” “crosslinked,” “at least partially cured,” and “at least partially crosslinked” refer to a composition having at least 2 wt % insolubles based on the total weight of the composition. In one or more embodiments, the compositions described herein can be cured to a degree so as to provide at least 3 wt %, or at least 5 wt %, or at least 10 wt %, or at least 20 wt %, or at least 35 wt %, or at least 45 wt %, or at least 65 wt %, or at least 75 wt %, or at least 85 wt %, or less than 95 wt % insolubles using Xylene as the solvent by Soxhlet extraction.

In a particular embodiment, the crosslinking is accomplished by exposing the grafted elastomeric composition to water (“moisture cure”). The grafted, elastomeric composition can be moisture cured after shaping or extruding the article or before shaping or extruding the article.

EXAMPLES

The foregoing discussion can be further described with reference to the following non-limiting examples. Grafted, elastomeric compositions containing at least one propylene-based copolymer in accordance with one or more embodiments described were prepared.

Table 1 summarizes the formulations of the compositions. Each composition was prepared in a Brabender thermoplastic compounder. The pellets of the copolymer were dried in a vacuum at over 50° C. for 4 hours to remove any moisture. The dried pellets and the thermoplastic component were charged into the Brabender in the presence of a nitrogen blanket at a melt temperature of 180° C. for 3 minutes to obtain a homogenous blend. The blends were then molded into 2 mm thick pads with 12 cm×14 cm dimensions on a compression molding press.

TABLE 1 Formulations in weight percent. Material EX. 1 EX. 2 EX. 3 EX. 4 EX. 5 EX. 6 VM6102 99.8 97.8 95 92.8 95 92.8 Slifin 06 2 2 2 PP5341 5 5 PP 9122 5 5 Irgafos 168 0.2 0.2 0.2 0.2 0.2 0.2 Total PHR 100.00 100.00 100.20 100.00 100.20 100.00

PCP-01 is a metallocene catalyzed propylene/ethylene copolymer having 16 wt % of ethylene. The MFR (2.16 kg at 230° C.) was 3 g/10 min.

SILFIN 06 is a commercially available silane crosslinking mixture (vinyltrimethoxy silane 85-88 wt %; dicumyl peroxide ˜8 wt %; and dibutyltin dilaurate ˜4 wt %) from Degusa.

PP 5341 is a 0.8 MFR (230° C., 2.16 kg) isotactic polypropylene (iPP) that is commercially available from ExxonMobil Chemical Company.

RCP 9122 is a random copolymer containing 2-3 wt % of ethylene derived units, the balance is propylene. The RCP 9122 has a MFR (2.16 kg at 230° C.) of 2.1 g/10 min and a density of 0.9 g/cm³. The 1% secant flexural modulus is 140 kPsi, as measured by ASTM D790A. RCP 9122 is commercially available from ExxonMobil Chemical Company.

Irgafos 168 is an antioxidant that is commercially available from Ciba Specialty Chemicals.

The vinyl grafted propylene-based copolymer containing the crosslinking catalyst was molded into 2 mm thick pads with 12 cm×14 cm dimensions on a compression molding press in the absence of moisture. The plaques thus prepared were placed in a hot water bath maintained at 50° C. for 2 hours to effect crosslinking.

Mechanical properties of the plaques before and after curing were evaluated. The test methods included ISO 878 for Hardness, ISO 37 for ultimate tensile strength (UTS) and ultimate elongation (UE), and ASTM D412 standard guidelines. The tension set of the blends were tested according to ASTM D412 at room temperature and 70° C. For room temperature and 70° C. testing for tension set the sample was aged at the test temperature for 30 minutes under 50% tension on Jig and annealed at room temperature for 30 minute after removing from the Jig. A xylene Soxhlet solvent extraction test was conducted according to ASTM D5492 on the cured samples using a Soxhlet extractor (extraction time=12 hrs) to understand the level of crosslinked material after e-beam curing. Results are expressed as: percent Xylene insoluble=weight after extraction/weight before extraction*100. The amount of insoluble gel before e-beam radiation crosslinking was practically undetectable by this method. Table 2 summarizes the mechanical properties of the plaques. Examples 1, 3, and 5 show the results without moisture cure and Examples 2, 4, and 6 show the results after moisture cure.

TABLE 2 Mechanical properties of the plaques. TESTED PROPERTIES Comparative Comparative EX. 4 Comparative (compression EX. 1 (without EX. 2 (after EX. 3 (without (after EX. 5 (without EX. 6 (after molded plaques) moisture cure) moisture cure) moisture cure) moisture cure) moisture cure) moisture cure) Hardness, Shore 61 61 61 66 61 69 A, 15 s. UTS (MPa), NA NA 9 9 10 12 (PSL Type 4 die) Strain at break, % NA NA 793.0 871.0 776.2 867.7 Peak stress, (MPa) 11.9 9.6 12.4 9.4 12.6 12.5 Peak Elongation, (%) 840.0 860.0 840.0 860.0 840.0 880.0 100% Mod. (MPa) 1.8 1.8 1.8 2.1 1.7 2.4 Tear strength, N/mm 28.1 29.3 30.0 33.6 28.2 39.5 Tension Set (%), 6.7 6.5 5.0 7.5 4.3 5.7 23 C. (Akron) Tension Set (%), 44 34 44 37 49 43 70 C. (Akron) MFR (230 C., 2.2 2.4 2.2 2.16 kg) (SEB) Xylene extraction, 0.0 44 0 26.9 3.1 22.1 Wt % insoluble

Peroxides tend to act as chain-breaking agents toward polypropylenes. However, it was surprisingly found that propylene-based polymers and blends thereof can be grafted with hydrolysable silane moieties that can be further crosslinked through condensation reactions. These compositions are suitable for preparing crosslinked articles with improved elastic and thermal performance compared to the uncrosslinked compositions.

For purposes of convenience, various specific test procedures are identified above for determining certain properties such as tensile set, percent elongation at break, Shore A Hardness, and toughness. However, when a person of ordinary skill reads this patent and wishes to determine whether a composition or polymer has a particular property identified in a claim, then any published or well-recognized method or test procedure can be followed to determine that property, although the specifically identified procedure is preferred. Each claim should be construed to cover the results of any of such procedures, even to the extent different procedures can yield different results or measurements. Thus, a person of ordinary skill in the art is to expect experimental variations in measured properties that are reflected in the claims. All numerical values can be considered to be “about” or “approximately” the stated value, in view of the nature of testing in general.

Certain embodiments and features have been described using a set of numerical upper limits and a set of numerical lower limits. It should be appreciated that ranges from any lower limit to any upper limit are contemplated unless otherwise indicated. Certain lower limits, upper limits and ranges appear in one or more claims below. All numerical values are “about” or “approximately” the indicated value, and take into account experimental error and variations that would be expected by a person having ordinary skill in the art.

To the extent a term used in a claim is not defined above, it should be given the broadest definition persons in the pertinent art have given that term as reflected in at least one printed publication or issued patent. Furthermore, all patents, test procedures, and other documents cited in this application are fully incorporated by reference to the extent such disclosure is not inconsistent with this application and for all jurisdictions in which such incorporation is permitted.

Further embodiments include:

1. A method for making a crosslinked elastomeric article, comprising:

-   -   blending an elastomeric composition comprising:         -   at least one propylene-based polymer comprising propylene             derived units and one or more dienes, the propylene-based             polymer having a triad tacticity of from 50% to 99% and a             heat of fusion of less than 80 J/g;         -   about 0.5 wt % to about 10 wt % vinyl siloxane; and         -   about 0.1 wt % to about 1.0 wt % peroxide,     -   extruding the blended composition; and     -   crosslinking the extruded polymer at a temperature of at least         about 50° C. and a relative humidity of at least about 90%.         2. The method of claim 1, further comprising extruding the         composition prior to crosslinking.         3. The method of claim 1 or 2, wherein the blended composition         further comprises one or more free radical initiators and one or         more condensation catalysts.         4. The method of any of claims 1-3, wherein the blended         composition further comprises one or more secondary elastomeric         components, one or more polyolefinic thermoplastic resins, or at         least one of each.         5. The method of any of claims 1-4, wherein the propylene-based         polymer has a heat of fusion from about 1 J/g to about 70 J/g.         6. The method of any of claims 1-5, wherein the propylene-based         polymer has a melting point of about 100° C. or less.         7. The method of any of claims 1-6, wherein the propylene-based         polymer has a triad tacticity from about 60% to about 97%.         8. The method of any of claims 1-7, wherein the propylene-based         polymer further comprises units derived from an alpha-olefin         other than the propylene derived units and the one or more         dienes in an amount from about 5 wt % to about 40 wt %.         9. The method of claim 8, wherein the propylene-based polymer         comprises units derived from ethylene, butene, hexene and/or         octene.         10. The method of claim 9, wherein the propylene-based polymer         comprises from about 5 wt % to about 40 wt % of units derived         from ethylene and/or butene.         11. The method of claim 9, wherein the propylene-based polymer         comprises from about 5 wt % to about 40 wt % of units derived         from ethylene and/or hexene.         12. The method of any of claims 1-4, wherein the propylene-based         polymer comprises of from about 0.2 to about 4 wt %         5-ethylidene-2-norbornene (ENB).         13. The method of any of claims 1-12, wherein the extruded         article is a fiber, yarn, or film.         14. A method for making a crosslinked elastomeric article,         comprising:     -   blending an elastomeric composition comprising:         -   at least one propylene-based polymer comprising propylene             derived units and one or more dienes, the propylene-based             polymer having a triad tacticity of from 50% to 99% and a             heat of fusion of less than 80 J/g;         -   one or more polyolefinic thermoplastic components;         -   about 0.5 wt % to about 10 wt % vinyl siloxane;         -   about 0.1 wt % to about 1.0 wt % peroxide; and         -   about 0.01 wt % to about 5 wt % condensation catalyst;     -   extruding the blended composition;     -   crosslinking the extruded polymer at a temperature of at least         about 50° C. and a relative humidity of at least about 90%.         15. The method of claim 14, wherein the blended composition         further comprises one or more secondary elastomeric components,         and wherein the one or more polyolefinic thermoplastic         components comprises isotactic polypropylene, random copolymer,         and impact copolymer.         16. A fiber made from the composition of claim 14.         17. A crosslinked elastomeric composition, comprising:     -   of from about 51 wt % to about 90 wt % at least one         propylene-based polymer comprising propylene derived units and         one or more dienes, the propylene-based polymer having a triad         tacticity of from 50% to 99% and a heat of fusion of less than         80 J/g;     -   of from about 0.5 wt % to about 10 wt % vinyl siloxane;     -   of from about 0.1 wt % to about 1.0 wt % peroxide;     -   of from about 5 wt % to about 40 wt % one or more polyolefinic         thermoplastic components; and     -   optionally of from about 5 wt % to about 40 wt % one or more         secondary elastomeric components, wherein the crosslinked         polypropylene has greater than 50% xylene insolubles as measured         according to ASTM-D 5492.         18. A fiber made from the crosslinked composition of claim 17.         19. A film made from the crosslinked composition of claim 17.         20. A film made from the composition of claim 14.

While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow. 

1. A method for making a crosslinked elastomeric article, comprising: blending an elastomeric composition comprising: at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; about 0.5 wt % to about 10 wt % vinyl siloxane; and about 0.1 wt % to about 1.0 wt % peroxide, extruding the blended composition; and crosslinking the extruded polymer at a temperature of at least about 50° C. and a relative humidity of at least about 90%.
 2. The method of claim 1, further comprising extruding the composition prior to crosslinking.
 3. The method of claim 2, wherein the blended composition further comprises one or more free radical initiators and one or more condensation catalysts.
 4. The method of claim 3, wherein the blended composition further comprises one or more secondary elastomeric components, one or more polyolefinic thermoplastic resins, or at least one of each.
 5. The method of claim 1, wherein the propylene-based polymer has a heat of fusion from about 1 J/g to about 70 J/g.
 6. The method of claim 1, wherein the propylene-based polymer has a melting point of about 100° C. or less.
 7. The method of claim 1, wherein the propylene-based polymer has a triad tacticity from about 60% to about 97%.
 8. The method of claim 1, wherein the propylene-based polymer further comprises units derived from an alpha-olefin other than the propylene derived units and the one or more dienes in an amount from about 5 wt % to about 40 wt %.
 9. The method of claim 1, wherein the propylene-based polymer comprises units derived from ethylene, butene, hexene and/or octene.
 10. The method of claim 1, wherein the propylene-based polymer comprises from about 5 wt % to about 40 wt % of units derived from ethylene and/or butene.
 11. The method of claim 1, wherein the propylene-based polymer comprises from about 5 wt % to about 40 wt % of units derived from ethylene and/or hexene.
 12. The method of claim 1, wherein the propylene-based polymer comprises of from about 0.2 to about 4 wt % 5-ethylidene-2-norbornene (ENB).
 13. The method of claim 1, wherein the extruded article is a fiber, yarn, or film.
 14. A method for making a crosslinked elastomeric article, comprising: blending an elastomeric composition comprising: at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; one or more polyolefinic thermoplastic components; about 0.5 wt % to about 10 wt % vinyl siloxane; about 0.1 wt % to about 1.0 wt % peroxide; and about 0.01 wt % to about 5 wt % condensation catalyst; extruding the blended composition; crosslinking the extruded polymer at a temperature of at least about 50° C. and a relative humidity of at least about 90%.
 15. The method of claim 14, wherein the blended composition further comprises one or more secondary elastomeric components, and wherein the one or more polyolefinic thermoplastic components comprises isotactic polypropylene, random copolymer, and impact copolymer.
 16. A fiber made from the composition of claim
 14. 17. A crosslinked elastomeric composition, comprising: of from about 51 wt % to about 90 wt % at least one propylene-based polymer comprising propylene derived units and one or more dienes, the propylene-based polymer having a triad tacticity of from 50% to 99% and a heat of fusion of less than 80 J/g; of from about 0.5 wt % to about 10 wt % vinyl siloxane; of from about 0.1 wt % to about 1.0 wt % peroxide; of from about 5 wt % to about 40 wt % one or more polyolefinic thermoplastic components; and optionally of from about 5 wt % to about 40 wt % one or more secondary elastomeric components, wherein the crosslinked polypropylene has greater than 50% xylene insolubles as measured according to ASTM-D
 5492. 18. A fiber made from the crosslinked composition of claim
 17. 19. A film made from the crosslinked composition of claim
 17. 20. A film made from the composition of claim
 14. 